One-Transistor Random Access Memory Technology Compatible with Metal Gate Process

ABSTRACT

One-transistor RAM technology compatible with a metal gate process fabricates a metal gate electrode formed of the same metal material as a top electrode of a MIM capacitor embedded isolation structure. A gate dielectric layer is formed of the same high-k dielectric material as a capacitor dielectric of the MIM capacitor embedded isolation structure.

This application is a divisional of patent application Ser. No. 10/896,491, entitled “One-Transistor Random Access Memory Technology Compatible with Metal Gate Process,” filed on Jul. 22, 2004, which application is incorporated herein by reference.

TECHNICAL FIELD

The present invention relates to a memory technology, and particularly to a metal gate process compatible with a metal-insulator-metal (MIM) capacitor process.

BACKGROUND

Typical memory cells are created comprising one single Metal-Oxide-Semiconductor Field-Effect-Transistor (MOS-FET) as a switching device connected with a capacitor as a digital data storage device, thus commonly referred to as a 1T-RAM device. A capacitor known as a metal-insulator-metal (MIM) structure possesses a low-interfacial reaction specificity to enhance its performance. The MIM capacitor has therefore become an important topic of research for memory technology. Leung, et al., “The Ideal SoC Memory: 1T-SRAM” 0-7803-6598 4/00, IEEE pp. 32 to 36, is incorporated herein by reference. U.S. Pat. No. 6,096,597 to Tsu, et al., U.S. Pat. No. 6,329,234 to Ma, et al., and U.S. Pat. No. 6,271,084 to Tu, et al. also incorporated herein by reference, describe MIM capacitor processes.

A gate electrode of the MOS transistor serves as part of that memory device wiring. As feature sizes of semiconductor devices continue to be scaled to smaller dimensions, it is desirable to reduce the resistance of gate electrode lines as much as possible, and the use of conventional gate electrode material is becoming increasingly problematic. In particular, the use of the gate electrode to align source/drain implants imposes significant limitations on the gate electrode material, such as polysilicon, which can withstand high temperatures of the source/drain annealing and prevent dopants from reacting with the channel region of the underlying silicon substrate. However, the polysilicon gate electrode has drawbacks of polysilicon depletion, voltage leakage, and high resistance. In an effort to overcome these problems, metals or refractory metal alloys are alternative materials currently being investigated for use as gate electrodes. These metallic materials offer potential advantages over polysilicon because of their pattern ability, low sheet resistance, and scalability to advanced MOS technologies. U.S. Pat. No. 6,001,716 for “Fabrication Method of a Metal Gate,” incorporated herein by reference, discloses a metal gate including a plurality of titanium nitride layers.

SUMMARY OF THE INVENTION

Embodiments of the present invention include a 1T-RAM technology compatible with a metal gate process to form a metal gate electrode and a MIM capacitor embedded isolation structure for improved electrical performance and simplified processing. In certain advantageous embodiments of the present invention, the metal gate electrode is formed of the same metal materials as a top electrode of the MIM capacitor embedded isolation structure. Also, a gate dielectric layer is formed of the same dielectric material as a capacitor dielectric of the MIM capacitor embedded isolation structure.

In one aspect, the present invention provides for a semiconductor device having a substrate with a first region and a second region. An isolation structure is formed in the substrate of the first region. A capacitor embedded in the isolation structure comprises a bottom electrode layer, a capacitor dielectric layer formed overlying the bottom electrode layer, and a top electrode layer formed overlying the capacitor dielectric layer. A transistor formed overlying the substrate of the second region comprises a gate dielectric layer and a gate electrode layer formed overlying the gate dielectric layer. The top electrode layer is formed of the same metal material as the gate electrode layer. The capacitor dielectric layer is formed of the same metal material as the gate dielectric layer.

In another aspect, the present invention provides for a fabrication method for a self-aligned metal gate electrode, comprising the steps as follows. A substrate is provided with a first trench isolation structure and a second trench isolation structure. A transistor is formed overlying the substrate outside the first trench isolation structure and the second trench isolation structure, wherein the transistor comprises a dummy gate dielectric layer and a dummy gate electrode layer formed overlying the dummy gate dielectric layer. A first dielectric layer is formed overlying the substrate to cover the first trench isolation structure and the second trench isolation structure and surround the transistor. A first trench and a second trench pass through the first dielectric layer to reach a portion of the first trench isolation structure and a portion of the second trench isolation structure, respectively. A first metal layer is formed on the sidewall and bottom of the first trench and the second trench, respectively. The dummy gate electrode layer and the dummy gate dielectric layer are removed to form an opening in the first dielectric layer. A second dielectric layer is formed overlying the substrate to cover the first metal layer and the sidewall and bottom of the opening. A second metal layer is formed overlying the second dielectric layer to fill the first trench, the second trench and the opening. Portions of the second metal layer and the second dielectric layer are removed until the second metal layer remaining in the first trench and the second trench is leveled off with, i.e., made planar to, the second metal layer remaining in the opening. The second metal layer remaining in the opening serves as a self-aligned gate electrode.

BRIEF DESCRIPTION OF THE DRAWINGS

The aforementioned preferred embodiments, features and advantages of this invention will become apparent by referring to the following detailed description of the preferred embodiments with reference to the accompanying drawings, wherein:

FIGS. 1-15 are pictorial diagrams illustrating an exemplary embodiment of a MIM capacitor process compatible with a metal gate process according to the present invention; and

FIG. 16 is a pictorial diagram illustrating an embodiment of a dual-STI design in the 1T-RAM technology according to the present invention.

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

The present invention provides 1T-RAM technology compatible with a metal gate process, which overcomes the aforementioned problems of the prior art arising from the use of polysilicon gate electrodes. Particularly, the metal gate process is compatible with a MIM capacitor embedded isolation structure to fabricate a metal gate electrode formed of the same metal material as a top electrode during the same deposition and patterning procedures. The integrated process for the metal gate electrode and the MIM capacitor embedded isolation structure has wide applicability to many manufacturers, factories and industries, and is potentially suited to a wide range of semiconductor device applications, for example mixed-mode integrated circuits, radio frequency (RF) circuits, static random access memory (SRAM), and dynamic random access memory (DRAM) technologies.

Reference will now be made in detail to the present embodiments, examples of which are illustrated in the accompanying drawings. Wherever possible, the same reference numbers are used in the drawings and the description to refer to the same or like parts. In the drawings, the shape and thickness of an embodiment may be exaggerated for clarity and convenience. This description will be directed in particular to elements forming part of, or cooperating more directly with, an apparatus in accordance with the present invention. It is to be understood that elements not specifically shown or described may take various forms well known to those skilled in the art. Further, when a layer is referred to as being on another layer or “on” a substrate, it may be directly on the other layer or on the substrate, or intervening layers may also be present.

Herein, cross-sectional diagrams of FIGS. 1-6, 8 and 11-14 and three-dimensional diagrams of FIGS. 7, 9-10 and 15 illustrate an exemplary embodiment of a 1T-RAM technology compatible with a metal gate process according to the present invention.

In FIG. 1, a substrate 10 has a memory cell array region 12 and a peripheral circuit region 14, which are isolated by respective shallow trench isolation (STI) structures 16 and 18. In the context of this disclosure, the term “substrate” refers to any supporting structures, including, but not limited to, a semiconductor substrate, a semiconductor wafer, and any construction comprising semiconductor material layers. The memory cell array region 12 is for the use of a 1T-RAM cell, and the peripheral circuit region 14 is a logic region for the use of core circuits or I/O circuits. In one embodiment, the STI structure 16 on the memory cell array region 12 has a depth d1 approximately equal to a depth d2 of the STI structure 18 on the peripheral circuit region 14. The depth d1 may vary from about 2500 to about 4500 angstroms, and the depth d2 may vary from about 2500 to about 4500 angstroms. The STI structures 16 and 18 may be created with conventional approaches, including, but not limited to, steps of etching trenches into the substrate, depositing isolating materials (oxide, nitride or combinations thereof) into the trenches, polishing off the excess isolating materials, and planarizing the trenches for the next level of fabrication.

Dummy transistors are provided on the memory cell array region 12 and the peripheral circuit region 14 as described below. In one embodiment, dummy gate electrode layers 22 and 24 are formed on respective dummy gate dielectric layers 20 and integrated with processes for forming sidewall spacers 26, lightly doped drain (LDD) regions 28, source/drain regions 30, and metal silicide layers 34. The material used to form the dummy gate electrode layers 22 and 24 may include, for example polysilicon, metal, metal alloys, and other suitable conductive materials. Alternatively, masking materials typically used for dopant implantation alignment, such as SiN, SiON, SiC and the like may be used to form the dummy gate electrode layers 22 and 24. The dummy gate dielectric layer 20 may include silicon oxide, silicon nitride, silicon oxynitride, silicon carbide, or other suitable dielectrics. The sidewall spacer 26 may include, for example, silicon oxide, silicon nitride, silicon oxynitride, or a combination thereof. The metal silicide layer 34 may include WSi, CoSi, NiSi, or TiSi. Fabrication methods of the dummy transistors shown in FIG. 1 are conventionally well known and no further detailed discussion is necessary.

As shown in FIG. 2, a first dielectric layer 36 is deposited on the substrate 10 to fill the space between adjacent dummy transistors through any of a variety of techniques, including LPCVD (low-pressure chemical vapor deposition), APCVD (atmospheric-pressure chemical vapor deposition), PECVD (plasma-enhanced chemical vapor deposition), spin-on coating, and future-developed deposition procedures. The material used to form the first dielectric layer 36 may include, for example, silicon oxide, silicon nitride, silicon oxynitride, low-k dielectric materials, other isolating materials, or combinations thereof. Next, an anisotropic etching process, i.e., an etch back process, or a planarization technology, i.e., CMP (chemical mechanical polish) process, may be employed to remove the excess portion of the first dielectric layer 36 until the first dielectric layer 36 is leveled off with the dummy gate electrode layers 22 and 24.

Through lithography, masking and dry etching techniques, capacitor trenches are then etched into the STI structures 16 of the memory cell array region 12 as set forth in FIGS. 3 and 4. A first photoresist layer 38 is provided on the first dielectric layer 36 to fully cover the peripheral circuit region 14, but only partially cover the memory cell array region 12. In detail, the first photoresist layer 38 has first openings 39 for defining respective capacitor trench patterns on the memory cell array region 12. Then, dry etch processes such as RIE (Reactive Ion Etching) and other plasma etching processes may be performed to form capacitor trenches 40 as shown in FIG. 4. Portions of the first dielectric layer 36 and STI structures 16 exposed under the first openings 39 are removed until the bottom thickness T of the respective STI structures 16 reaches from about 500 angstroms to about 3000 angstroms. The first photoresist layer 38 is then stripped off from the first dielectric layer 36. Thus, the capacitor trench 40 exposes portions of the STI structure 16 and the substrate 10 adjacent to the source/drain regions 30. The opening diameter of the capacitor trench 40 is a matter of design choice dependent on product requirements and process limitations.

Through metal deposition and etch back techniques, a bottom electrode 42 a is formed along the bottom and sidewall of the capacitor trench 40 as shown in FIGS. 5 and 6. Referring to FIG. 5, a first metal layer 42 is conformally formed on the substrate 10 by a blanket deposition. The first metal layer 42 may include a single-metal layer, a dual-metal stack or a multi-layered stack, selected from W, WN, Ti, TiW, TiN, Ta, TaN, Al, Cu, Mo, or the like. The blanket deposition for the first metal layer 42 may include, but is not limited to, CVD, PVD (physical vapor deposition), evaporation, plating, ALD (atomic layer deposition), or combinations thereof. The deposition conditions allow for continuous coverage of the first metal layer 42 over the sidewall of the capacitor trench 40 without affecting its electrical characteristics during and after its deposition. The thickness of the first metal layer 42 may vary from about 50 angstroms to about 500 angstroms. Referring to FIG. 6, the first metal layer 42 outside the capacitor trenches 40 is then removed by CMP or etch back technologies, thus the first metal layer 42 remaining along the sidewall and bottom of the capacitor trench 40 serves as a bottom electrode 42 a. FIG. 7 is a three-dimensional diagram illustrating an exemplary array of the bottom electrodes 42 a formed in respective capacitor trenches 40, and FIG. 6 is a cross-sectional view along line 6-6 of FIG. 7.

After patterning the bottom electrodes 42 a, a micro-trench process for a connection path between adjacent capacitors is now described in FIGS. 8-11. FIG. 8 is a cross-sectional diagram along line 8-8 of FIG. 9, and FIG. 11 is a cross-sectional diagram along line 11-11 of FIG. 10.

Referring to FIGS. 8 and 9, a second photoresist layer 44 is formed on the substrate 10 to provide a second opening 45 for defining at least one micro-trench pattern on the memory cell array region 12. In one embodiment, each bottom electrode 42 a comprises two non-continuous portions 42 b and 42 c, and the second opening 45 exposes the portions 42 b and 42 c and the first dielectric layer 36 there between, thus defining a connection path between adjacent capacitors. The profile and size of the second opening 45 are design choices dependent on electrical connection paths among MIM capacitors. The second opening 45 may include, but is not limited to, for example, stripe-shaped openings, curve-shaped openings, sawtooth-shaped openings, or other geometric openings arranged in parallel, in perpendicular, in an uncrossed format, or in an intersected format. In an exemplary embodiment as shown in FIG. 9, the second opening 45 comprises stripe-shaped openings, and each stripe-shaped opening crosses a plurality of capacitor trenches 40 substantially aligned in a direction along the dummy gate electrode layer 22. Next, in FIG. 10, dry etch processes, such as RIE and other plasma etching processes, allow production of micro-trench patterns 43 that are etched into the non-continuous portions 42 b and 42 c and the first dielectric layer 36 there between to reach a predetermined depth d4 and a predetermined width w. The second photoresist layer 44 is then stripped from the substrate 10, and thereby the bottom electrodes 42 a and the capacitor trenches 40 are exposed again as shown in FIG. 11. The depth d4 may vary from about 0.05 angstroms to 0.3 angstroms, and the width w may vary from about 100 angstroms to 1500 angstroms. Depending on product requests and process limitations, the profile, size and amount of the micro-trench patterns 43 are design choices. The purpose of fabricating the micro-trench patterns 43 is to create a connection trench across upper portions of adjacent top electrodes being fabricated in subsequent processes.

Before proceeding with forming capacitor dielectrics and top electrodes of the MIM capacitors, the dummy gate electrode layers 22 and 24 and the dummy gate dielectric layers 20 are successively removed from the memory cell array region 12 and the peripheral circuit region 14 through lithography, masking, dry etch or other selective etching processes dependent on the materials used for the layers 22, 24 and 20. As a result, in FIG. 12, third openings 46 surrounded by the sidewall spacers 26 and the first dielectric layer 36 are formed to expose the substrate 10. The third openings 46 define areas for self-aligned metal gate electrodes on the memory cell array region 12 and the peripheral circuit region 14.

The MIM capacitor process for capacitor dielectrics and top electrodes now proceeds in FIGS. 13-15. In FIG. 13, a second dielectric layer 48 is conformally deposited on the substrate 10 through any of a variety of deposition techniques, including CVD, LPCVD, APCVD, PECVD, ALD and the like. Particularly, the second dielectric layer 48 covers the bottom electrodes 42 a, the micro-trench patterns 43 and the third openings 46. The material used to form the second dielectric layer 48 may include a high-k material. The term “high-k” as used herein denotes a dielectric that has a dielectric constant (k) of greater than about 4.0, preferably from about 8 to about 50. It is noted that all the dielectric constants disclosed herein are relative to a vacuum, unless otherwise stated. A wide variety of high-k dielectrics may be employed, including but not limited to: binary metal oxides such as Ta₂O₅, HfO₂, Al₂ 0 ₃, InO₂, La₂O₃, ZrO₂ and TaO₂; silicates, aluminates and oxynitrides of said binary metal oxides; and perovskite-type oxides. Combinations and/or multilayers of such high-k dielectrics are also contemplated herein. The second dielectric layer 48 preferably has a thickness of from about 10 to about 250 angstroms. In a preferred embodiment, the second dielectric layer 48 is a Ta₂O₅ layer.

Successively, a second metal layer 50 is formed on the second dielectric layer 48 to fill the fourth openings 46, the capacitor trenches 40 and the micro-trench patterns 43. The second metal layer 50 may be a single-metal layer, a dual-metal structure or a multi-layered structure selected from at least one of W, WNx, Ti, TiWx, TiNx, Ta, TaNx, Mo, Al, Cu, and the like. The suffix “x” can be modified to adjust the work function of the gate electrode. Any of a variety of deposition techniques, including, but not limited to, CVD, PVD, evaporation, plating, sputtering, reactive co-sputtering or combinations thereof, may allow the production of the second metal layer 50. In a preferred embodiment, the second metal layer 50 is a TiN/W/Cu multi-layered structure. In another preferred embodiment, the second metal layer 50 is a TiN/W dual-layered structure.

In FIG. 14, an etch back or a CMP process may be performed to remove portions of the second metal layer 50 and the second dielectric layer 48 until the top of the first dielectric layer 36 is exposed and leveled off with the second metal layer 50. As a result, a portion 50 a of the second metal layer 50 remaining in the capacitor trench 40 serves as a top electrode 50 a, and a portion 48 a of the second dielectric layer 48 sandwiched between the bottom electrode 42 a and the top electrode 50 a serves as a capacitor dielectric 48 a, thus MIM capacitors 52 are completed in the respective STI structures 16, referring to a MIM capacitor embedded isolation structure. Also, portions 50I and 50II of the second metal layer 50 remaining in the third openings 46 serve as self-aligned metal gate electrodes 50I and 50II, respectively. The portions 48″ of the second dielectric layer 48 surrounding the bottom and sidewalls of the metal gate electrodes 50I and 50II serve as gate dielectrics thereof, respectively. The metal gate electrodes 50I and 50II integrated with the high-k gate dielectrics 48″ are therefore completed on the memory cell array region 12 and the peripheral circuit region 14. In addition, a portion 50 b remaining in the micro-trench patterns 43 serves as a connection pad 50 b which can couple upper portions of adjacent top electrodes 50 a together as shown in FIG. 15.

FIG. 15 is a three-dimensional diagram illustrating a connection path among the top electrodes 50 a of adjacent MIM capacitors 52. Capacitor dielectrics 48 a are omitted in FIG. 15 for clarity. FIG. 14 is a cross-sectional diagram along line 14-14 of FIG. 15. For example, the top electrodes 50 a of the MIM capacitors 52 aligned in a line can be connected through the connection pads 50 b. The connection pads 50 b may be leveled off with the top electrodes 50 a and the metal gate electrodes 50I and 50II.

Accordingly, a fabrication method for 1T-RAM technology has been presented that allows for a metal gate electrode formed of the same metal material as a top electrode of a MIM capacitor, and allows for a gate dielectric layer formed of the same high-k dielectric material as a capacitor dielectric. Thus, the MIM capacitor process can be fully compatible with the metal gate process to offer process cost competitiveness. Also, the fabrication method creates connection pads in micro-trench patterns across adjacent MIM capacitors, thus corresponding top electrodes can be electrically connected to each other. Moreover, the metal gate electrodes formed on the memory cell array region and the logic peripheral region have advantages of their pattern ability, low sheet resistance, good thermal reliability, excellent current flow, less voltage depletion problems than polysilicon, and scalability to advanced MOS technologies.

Embodiments of the present invention provide the MIM capacitor, which has a lower portion embedded in the STI structure and has an upper portion substantially leveled off with the metal gate electrode. The trench design for the MIM capacitor allows the formation of densely arranged memory cell arrays. The capacitance may be increased by providing a capacitor dielectric with a high permittivity, forming a capacitor dielectric of a large surface area, or using a thin capacitor dielectric. In an exemplary implementation of the present invention, one approach for improved capacitance is to provide a capacitor dielectric with a large surface area by increasing the depth of the capacitor trench. For example, the depth d1 of the STI structure 16 may be increased, and thereby capacitor trench 40 may extend to a deeper location.

FIG. 16 is a cross-sectional diagram illustrating an example of dual-STI design in the 1T-RAM technology compatible with the metal gate process, while explanation of the same or similar portions to the description in FIGS. 1-15 will be omitted. Compared with the STI structure 18 fabricated on the peripheral circuit region 14, a STI structure 16″ having a greater depth is created on the memory cell array region 12. For example, the STI structure 16″ has a depth D greater than the depth d2 of the STI structure 18. The depth D may vary from about 5000 to about 9000 angstroms, and the bottom thickness T of the STI structure 16″ reaches from about 500 angstroms to about 3000 angstroms. Thus, the capacitor dielectric 48 a has an increased surface area to contribute improved capacitance to the MIM capacitor 52.

Although the present invention has been described in its preferred embodiments, it is not intended to limit the invention to the precise embodiments disclosed herein. Those skilled in this technology can still make various alterations and modifications without departing from the scope and spirit of this invention. Therefore, the scope of the present invention shall be defined and protected by the following claims and their equivalents. 

1. A semiconductor device, comprising: a substrate having a first region and a second region; at least one isolation structure formed in said first region of said substrate; a capacitor embedded in said isolation structure, wherein said capacitor comprises a bottom electrode layer, a capacitor dielectric layer formed overlying said bottom electrode layer, and a top electrode layer formed overlying said capacitor dielectric layer; and at least one first transistor formed in said second region of said substrate, wherein said first transistor comprises a first gate dielectric layer and a first gate electrode layer formed overlying said first gate dielectric layer; wherein, said top electrode layer is formed of the same metal material as said first gate electrode layer.
 2. The semiconductor device of claim 1, wherein said capacitor dielectric layer is formed of the same dielectric material as said first gate dielectric layer.
 3. The semiconductor device of claim 2, wherein said capacitor dielectric layer and said first gate dielectric layer comprise a dielectric material having a dielectric constant of greater than 4.0.
 4. The semiconductor device of claim 2, wherein said capacitor dielectric layer and said first gate dielectric layer comprise a metal oxide layer.
 5. The semiconductor device of claim 1, wherein said semiconductor device comprises: a first isolation structure and a second isolation structure formed in said first region of said substrate; a first capacitor and a second capacitor embedded in said first isolation structure and said second isolation structure, respectively; wherein, said first capacitor comprises a first bottom electrode layer and a first top electrode layer; wherein, said second capacitor comprises a second bottom electrode layer and a second top electrode layer; and wherein, said first top electrode layer is electrically connected to said second top electrode layer through a connection pad formed in a connection trench across an upper portion of said first bottom electrode layer and an upper portion of said bottom electrode layer.
 6. The semiconductor device of claim 5, wherein said connection trench has a depth from about 0.05 angstroms to about 0.3 angstroms.
 7. The semiconductor device of claim 5, wherein said connection pad is formed of the same metal material as said first top electrode layer and said second top electrode layer.
 8. The semiconductor device of claim 1, wherein said top electrode layer is leveled off with said first gate electrode layer.
 9. The semiconductor device of claim 1, wherein said isolation structure is a trench isolation structure formed in said substrate.
 10. The semiconductor device of claim 1, wherein said substrate comprises a peripheral circuit region and a memory cell array region, and said first region and said second region are defined in said memory array region.
 11. The semiconductor device of claim 10, further comprising at least one second transistor formed in said peripheral circuit region of said substrate, wherein said second transistor comprises a second gate dielectric layer and a second gate electrode layer formed overlying said second gate dielectric layer.
 12. The semiconductor device of claim 11, wherein said second gate electrode layer is formed of the same metal material as said top electrode layer.
 13. The semiconductor device of claim 11, wherein said second gate dielectric layer is formed of the same dielectric material as said capacitor dielectric layer.
 14. The semiconductor device of claim 13, wherein said second gate dielectric layer comprises a dielectric material having a dielectric constant of greater than 4.0.
 15. The semiconductor device of claim 13, wherein said second gate dielectric layer comprises a metal oxide layer.
 16. The semiconductor device of claim 10, wherein: said substrate comprises at least one isolation structure in said memory cell array region; said substrate comprises at least one isolation structure in said peripheral circuit region; and said isolation structure formed in said memory cell array region has a depth substantially equal to a depth of said isolation structure formed in said peripheral region.
 17. The semiconductor device of claim 10, wherein: said substrate comprises at least one isolation structure in said memory cell array region; said substrate comprises at least one isolation structure in said peripheral circuit region; and said isolation structure formed in said memory cell array region has a depth greater than a depth of said isolation structure formed in said peripheral region.
 18. A memory cell, comprising: a substrate comprising a trench; a capacitor formed in said trench and comprising a bottom electrode layer, a capacitor dielectric layer formed overlying said bottom electrode layer, and a top electrode layer formed overlying said capacitor dielectric layer; and a transistor formed in said substrate outside said trench, wherein said transistor comprises a gate dielectric layer and a gate electrode layer formed overlying said gate dielectric layer; wherein, said top electrode layer is formed of the same metal material as said gate electrode layer; and wherein, said capacitor dielectric layer is formed of the same dielectric material as said gate dielectric layer.
 19. The memory cell of claim 18, wherein said capacitor dielectric layer and said gate dielectric layer comprise a dielectric material having a dielectric constant of greater than 4.0.
 20. The memory cell of claim 18, wherein said capacitor dielectric layer and said gate dielectric layer comprise a metal oxide layer.
 21. The memory cell of claim 18, wherein: said bottom electrode layer is formed along the sidewall and bottom of said trench; said capacitor dielectric layer is formed overlying said bottom electrode layer; said top electrode layer is formed overlying said capacitor dielectric layer to fill said trench; and said top electrode layer is substantially leveled off with said gate electrode layer.
 22. The memory cell of claim 18, wherein said substrate comprises an isolation structure in said trench, and said capacitor is formed overlying said isolation structure.
 23. The memory cell of claim 18, further comprising: a dielectric layer formed overlying said substrate and comprising at least one opening outside said trench; wherein, said gate dielectric layer is formed along the sidewall and bottom of said opening; and wherein, said gate electrode layer is formed overlying said gate dielectric layer to fill said opening.
 24. The memory cell of claim 18, wherein said gate dielectric layer surrounds the bottom and sidewalls of said gate electrode layer.
 25. A random access memory device, comprising: a substrate having a first region and a second region; at least one trench isolation structure formed in said first region of said substrate; a capacitor embedded in said trench isolation structure, wherein said capacitor comprises a bottom electrode layer, a capacitor dielectric layer formed overlying said bottom electrode layer, and a top electrode layer formed overlying said capacitor dielectric layer; and at least one transistor formed in said second region of said substrate, wherein said transistor comprises a gate dielectric layer and a gate electrode layer formed overlying said gate dielectric layer, wherein, said top electrode layer is formed simultaneously with and of the same metal material as said gate electrode layer.
 26. The random access memory device of claim 25, wherein said capacitor dielectric layer is formed simultaneously with and of the same dielectric material as said gate dielectric layer.
 27. The random access memory device of claim 26, wherein said capacitor dielectric layer and said gate dielectric layer comprise a dielectric material having a dielectric constant of greater than 4.0.
 28. The random access memory device of claim 25, further comprising: a first trench isolation structure and a second trench isolation structure formed in said first region of said substrate; and a first capacitor and a second capacitor embedded in said first trench isolation structure and said second trench isolation structure, respectively; wherein, said first capacitor comprises a first bottom electrode layer and a first top electrode layer; wherein, said second capacitor comprises a second bottom electrode layer and a second top electrode layer; and wherein, said first top electrode layer is electrically connected to said second top electrode layer through a connection pad formed in a connection trench across an upper portion of said first bottom electrode layer and an upper portion of said second bottom electrode layer.
 29. The random access memory device of claim 28, wherein said connection pad is formed simultaneously with and of the same metal material as said first top electrode layer and said second top electrode layer. 